Products
GL3019 ad optimum perficientur
Typus et applicationem
| Type | Productum | Application et commoda |
| GL3019 | PBT resinae | Secundarium Coating Materias pro Optica Fibra |
Depictio producti
PBT est magni ponderis secundae materias efficiens pro fibris opticis, Egregiam habet observantiam in proprietatibus mechanicis /thermalibus /hydrolyticis / chemicis resistentibus, et facile processit mechanica.
| Properties | commoda | Descriptio |
| Mechanica proprietatibus | Princeps stabilitas | Parva DECREMENTUM scala, parva volubilis in utendo, bona stabilitas in formando. |
| Princeps vi mechanica | Bonus modulus, bona extensio effectus, vis alta distrahens, pressionis lateralis laxatube altior est quam exigentia vexillum. | |
| Scelerisque possessiones | Princeps tortor tortor | Utrum in magno onere vel infimo onere , perfectio pravitatis optima est |
| proprietatibus hydrolytic | Anti-hydrolysis | Altus effectus funis makeoptical anti-hydrolysis longioris vitae quam exigentiae vexillum est. |
| Proprietates chemica | Resistentia chemica | PBT tolerare potest plurimam polaritatem chemicae reagentat locus temperatus.Et PBT non compatitur cum impletione gel.in caliditas ac suscipit exesa. |
Processus technology
| Zone | Extruderbody 1 | Extruderbody 2 | Extruderbody 3 | Extruderbody 4 | Extruderbody 5 | Flange | Extruderneck | Extruderhead 1 | Extruderhead 2 | Calida aqua | Aquae calidae |
| / | 240 | 245 | 250 | 255 | 255 | 255 | 250 | 245 | 245 | 45 | 20 |
Repono et onerariis
Sarcina: Duae sarcinae modi, : 1. 900/1000KG per sacculum refertum cum materia interiori liniationis aluminii ffoyle, linitio externa PE materia contexta.2
Transportatio: Pati non debet per translationem humiditatem vel humiditatem accipere, et eam siccam, mundam, integram et immunem custodire.Repono: Reponitur in puro, frigido, sicco et ventilato horreis a fonte ignis.Si productum inveniatur madefactum in ratione pluvioso vel magno humido in aere, adhiberi potest una hora postea postquam siccetur in temperie 120℃.
GL3019 possessiones
| Nec. | proprietatibus inspectis | Unitas | Standardrequirement | Typical | methodum inspectionem |
| 1 | Densitas | g/cm3 | 1.25 1.35 | 1.30 | GB/T1033-2008 |
| 2 | Exustio Index（250℃、2160g） | g/10min | 12.0 18.0 | 16.8 | GB/T3682-2000 |
| 3 | Humorem content | % | ≤0.05 | 0.03 | GB/T20186.1-2006 |
| 4 | Absorptio aquae | % | ≤0.5 | 0.3 | GB/T1034-2008 |
| 5 | Distrahentes vires in cede | MPa | ≥32 | 48.73 | GB/T1040.2-2006 |
| Prolongatio ad cede | % | 4.0 10 | 6.23 | GB/T1040.2-2006 | |
| Prolongatio ad intermissum | % | ≥100 | 162.5 | GB/T1040.2-2006 | |
| modulus distrahentes elasticitates | MPa | ≥1450 | 2053 | GB/T1040.2-2006 | |
| 6 | Flexurae modularis | MPa | ≥1450 | 2136 | GB/T9341-2000 |
| vires tendentes | MPa | ≥45 | 60.5 | GB/T9341-2000 | |
| 7 | Liquescens punctum | ℃ | 210 240 | 218 | DTA |
| 8 | Litore duritiem | - | ≥70 | 71 | GB/T2411-2008 |
| 9 | Izod impulsum 23℃ | KJ/m2 | ≥5.0 | 5.6 | GB/T1843-2008 |
| Izod impulsum -40℃ | KJ/m2 | ≥4.0 | 4.9 | GB/T1843-2008 | |
| 10 | Coefficiens linearexpansion 23～ 80℃） | 10-4K-1 | ≤1.5 | 1.26 | GB/T1036-1989 |
| 11 | Coefficiens volubilis resistentia | Ω.cm | ≥1×1014 | 3.1×1016 | GB/T1410-2006 |
| 12 | Heat distorsio temp 1.8M pa | ℃ | ≥55 | 57.2 | GB/T1634.2-2004 |
| Caloris pravitatis temp 0.45 M pa | ℃ | ≥170 | 173.7 | GB/T1634.2-2004 | |
| 13 | scelerisque hydrolysis | ||||
| Distrahentes vires in cede | MPa | ≥32 | 45.8 | GB/T1040.1-2006 | |
| Prolongatio ad intermissum | % | ≥10 | 36 | GB/T1040.1-2006 | |
| 14 | Compatibilitas inter materiam et saturitatem compositorum | ||||
| Distrahentes vires in cede | MPa | ≥32 | 46.8 | GB/T1040.1-2006 | |
| Prolongatio ad intermissum | % | ≥100 | 126.8 | GB/T1040.1-2006 | |
| 15 | Aspectus | GB/T2018.1-2006 3.1 | Secundum | GB/T20186.1-2006 | |
Nota: 1. Productum debet siccari et signati sarcina.Commendatur utendum calidum aerem ad vitandum humorem antequam utatur.temperatus intra -80~90）℃;
Innovatio scientifica et technica res gestae
Nunc, Jiangyin officinas VIII inventionis diplomata PBT modificata et polypropylene soluta bushings modificata, 38 exemplar patentes utilitatis habet, et in signis globi PBT formulam participavit.
Impetravi tria producta summi - tech producti certificationis.
Anno 2017, investigationem et progressionem centri materiae polymerorum in cooperatione cum Universitate Shanghai Jiao Tong stabilivit.
Mense Octobri MMXVIII, inceptum per Jiangsu provinciae summus tech agnitus est.
Progressionem novorum productorum augere et arctam materiam investigationis et evolutionis cooperationis mechanismi cum notis fune societatibus domi forisque componunt.